rust: Definition from Answers.com

Iron alloy phases v • d • e Ferrite (α-iron, δ-iron; soft) Austenite (γ-iron; harder) Spheroidite Pearlite (88% ferrite, 12% cementite) Bainite Martensite Ledeburite (ferrite-cementite eutectic, 4.3% carbon) Cementite (iron carbide, Fe3C; hardest) Steel classes Carbon steel (≤2.1% carbon; low alloy) Stainless steel (+chromium) Maraging steel (+nickel) Alloy steel (hard) Tool steel (harder) Other iron-based materials Cast iron (>2.1% carbon) Ductile iron Wrought iron (contains slag)

Rust on a chain fence

Rusted bolt

A blacksmith removing rust with sand prior to welding

Rust damage in automobiles can create hidden dangers.

Rusting can completely degrade iron. Note the galvanization on the unrusted portions.

Rust is a general term for a series of iron oxides, usually red oxides, formed by the reaction of iron and oxygen in the presence of water or air moisture. Several forms of rust are distinguishable visually and by spectroscopy, and form under different circumstances.^[1] Rust consists of hydrated iron(III) oxides Fe₂O₃·nH₂O, iron(III) oxide-hydroxide (FeO(OH), Fe(OH)₃. Rusting is the common term for corrosion of iron and its alloys, such as steel. Other metals undergo equivalent corrosion, but the resulting oxides are not commonly called rust. Given sufficient time, oxygen, and water, any iron mass eventually converts entirely to rust and disintegrates. The corrosion of aluminium is extremely slow because the resulting aluminium oxide forms a conformal coating, which protects the remaining aluminium. This process is known as passivation.

Chemical reactions

The Oxidation of Iron Metal

When in contact with water and oxygen, or other strong oxidant or acids, iron will rust. If salt is present, for example, in salt water, the metal rusts more quickly. This chemical reaction is used in the production of handwarmers^[2] Iron metal is relatively unaffected by pure water or by dry oxygen. As with other metals, a tightly adhering oxide coating, a passivation layer, protects the bulk iron from further oxidation. Thus, the conversion of the passivating iron oxide layer to rust results from the combined action of two agents, usually oxygen and water. Other degrading solutions are sulfur dioxide in water and carbon dioxide in water. Under these corrosive conditions, iron(III) species are formed. Unlike iron(II) oxides, iron(III) oxides are not passivating because these materials do not adhere to the bulk metal. As these iron(III) compounds form and flake off from the surface, fresh iron is exposed, and the corrosion process continues until all of the iron(0) is either consumed or all of the oxygen, water, carbon dioxide, or sulfur dioxide in the system are removed or consumed. ^[3]

Chemical reactions associated with rusting

The rusting of iron is an electrochemical process that begins with the transfer of electrons from iron to oxygen.^[4] The rate of corrosion is affected by water and accelerated by electrolytes, as illustrated by the effects of road salt (calcium chloride) on the corrosion of automobiles. The key reaction is the reduction of oxygen:

O₂ + 4 e^- + 2 H₂O → 4 OH^-

Because it forms hydroxide ions, this process is strongly affected by the presence of acid. Indeed, the corrosion of most metals by oxygen is accelerated at low pH. Providing the electrons for the above reaction is the oxidation of iron that may be described as follows:

Fe → Fe²⁺ + 2 e⁻

The following redox reaction also occurs in the presence of water and is crucial to the formation of rust:

4 Fe²⁺ + O₂ → 4 Fe³⁺ + 2 O²⁻[[1]]

Additionally, the following multistep acid-base reactions affect the course of rust formation:

Fe²⁺ + 2 H₂O ⇌ Fe(OH)₂ + 2 H⁺

Fe³⁺ + 3 H₂O ⇌ Fe(OH)₃ + 3 H⁺

as do the following dehydration equilibria:

Fe(OH)₂ ⇌ FeO + H₂O

Fe(OH)₃ ⇌ FeO(OH) + H₂O

2 FeO(OH) ⇌ Fe₂O₃ + H₂O

From the above equations, it is also seen that the corrosion products are dictated by the availability of water and oxygen. With limited dissolved oxygen, iron(II)-containing materials are favoured, including FeO and black lodestone (Fe₃O₄). High oxygen concentrations favour ferric materials with the nominal formulae Fe(OH)_3-xO_x/2. The nature of rust changes with time, reflecting the slow rates of the reactions of solids.

Furthermore, these complex processes are affected by the presence of other ions, such as Ca²⁺, which both serve as an electrolyte, and thus accelerate rust formation, or combine with the hydroxides and oxides of iron to precipitate a variety of Ca-Fe-O-OH species.

Rust prevention

Rust is permeable to air and water, therefore the interior iron continues to corrode. Rust prevention thus requires coatings that preclude rust formation. Stainless steel forms a passivation layer of chromium(III) oxide. Similar passivation behavior occurs with magnesium, copper, titanium, zinc, aluminium.

An important approach to rust prevention entails galvanization, which typically consists of an application, on the object to be protected, of a layer of zinc by either hot-dip galvanizing or electroplating. Zinc is traditionally used because it is cheap, adheres well to steel and provides a cathodic protection to the steel surface in case of damage of the Zinc layer. In more corrosive environments (such as salt water) cadmium is preferred. Galvanization often fails at seams, holes, and joints, where the coating is pierced. In these cases the coating provides cathodic protection to metal, where it acts as a galvanic anode rusting in preference. More modern coatings add aluminium to the coating as zinc-alume, aluminium will migrate to cover scratches and thus provide protection for longer. These approaches rely on the aluminium and zinc oxides protecting the once-scratched surface rather than oxidizing as a sacrificial anode. In some cases, very aggressive environments or long design life, both zinc and a coating are applied to provide corrosion protection.

Several other methods are available to control corrosion and prevent the formation of rust, colloquially termed rustproofing:

• Cathodic protection is a technique used to inhibit corrosion on buried or immersed structures by supplying an electrical charge that suppresses the electrochemical reaction. If correctly applied, corrosion can be stopped completely. In its simplest form it is achieved by attaching a sacrificial anode thus making the iron or steel the cathode in the cell formed. The sacrificial anode must be made made from something with a more negative electrode potential than the iron or steel, commonly zinc, aluminium or magnesium.
• Bluing is a technique that can provide limited resistance to rusting for small steel items, such as firearms; for it to be successful, water-displacing oil is rubbed onto the blued steel.
• Rust formation can be controlled with coatings, such as paint, that isolate the iron from the environment. Large structures with enclosed box sections, such as ships and modern automobiles, often have a wax-based product (technically a "slushing oil") injected into these sections. Such treatments also contain rust inhibitors. Covering steel with concrete provides protection to steel by the high pH environment at the steel-concrete interface.
• Another method to avoid rust is to control the environment. Controlling the humidity, if possible, below a certain thereshold can reduce or stop the corrosion process.
• Rusting can be controlled also by proper design, avoiding for example areas of stagnant water, galvanic coupling with more noble materials...
• Corrosion inhibitors, like gas phase or volatile inhibitors can be used to prevent corrosion in closed systems.
• A simple and inexpensive way to remove rust from steel surfaces by hand is to rub the steel with aluminium foil dipped in water. Aluminium has a higher reduction potential than the iron in steel, which may help transfer oxygen atoms from the iron to the aluminium. The aluminium foil is softer than steel and will not scratch it, as steel wool will, but as the aluminium oxidizes, the aluminium oxide produced becomes a fine metal polishing compound.^{[citation needed]}

Economic impact

Rust is associated with degradation of iron-based tools and structures. As rust has a much higher volume than the originating mass of iron, its build-up can also cause failure by forcing apart adjacent parts — a phenomenon sometimes known as "rust smacking". It was the cause of the collapse of the Mianus river bridge in 1983, when the bearings rusted internally and pushed one corner of the road slab off its support. Three drivers on the roadway at the time died as the slab fell into the river below. The following National Transportation Safety Board (NTSB) investigation showed that a drain in the road had been blocked for road re-surfacing, and had not been unblocked so that runoff water penetrated the support hangers. It was also difficult for maintenance engineers to see the bearings from the inspection walkway. Rust was also an important factor in the Silver Bridge disaster of 1967 in West Virginia, when a steel suspension bridge collapsed in less than a minute, killing 46 drivers and passengers on the bridge at the time.

Kinzua Bridge in Pennsylvania was blown down by a tornado in 2003 largely because the central base bolts holding the structure to the ground had rusted away, leaving the bridge resting by gravity alone.

Similarly corrosion of concrete-covered steel and iron can cause the concrete to spall, creating severe structural problems. It is one of the most common failure modes of reinforced concrete bridges.

See also

• Cosmoline
• List of bridge disasters
• Relevance to Tetanus
• Weathering steel
• WD-40

References

External links

• Corrosion Cost A site dedicated to the study of economic impact of Corrosion
• corrosion case studies Analysis of corrosion
• Corrosion Doctors Rusting article
• Metal Corrosion Rust What is Rust