US20180311943A1 - Multilayer composite films for architectural applications - Google Patents

  • ️Thu Nov 01 2018

US20180311943A1 - Multilayer composite films for architectural applications - Google Patents

Multilayer composite films for architectural applications Download PDF

Info

Publication number
US20180311943A1
US20180311943A1 US15/772,236 US201615772236A US2018311943A1 US 20180311943 A1 US20180311943 A1 US 20180311943A1 US 201615772236 A US201615772236 A US 201615772236A US 2018311943 A1 US2018311943 A1 US 2018311943A1 Authority
US
United States
Prior art keywords
layer
multilayer composite
composite film
etfe
major surface
Prior art date
2015-10-28
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/772,236
Inventor
Marina Temchenko
Martin Augustyniak
Sam Lim
Charles Robert Comeau, Jr.
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sc Innovation LLC
Madico Inc
Original Assignee
Sc Innovation LLC
Madico Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
2015-10-28
Filing date
2016-10-28
Publication date
2018-11-01
2016-10-28 Application filed by Sc Innovation LLC, Madico Inc filed Critical Sc Innovation LLC
2016-10-28 Priority to US15/772,236 priority Critical patent/US20180311943A1/en
2018-11-01 Publication of US20180311943A1 publication Critical patent/US20180311943A1/en
2019-11-26 Assigned to SC Innovation, LLC, MADICO, INC. reassignment SC Innovation, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: AUGUSTYNIAK, Martin, LIM, SAM, TEMCHENKO, MARINA
Status Abandoned legal-status Critical Current

Abstract

A multilayer composite film that includes an outer ETFE layer adhered to a polyethylene terephthalate (PET) layer. These layers are adhered together by a fluoropolymer adhesive. The multilayer composite film also include an infra-red (IR) radiation rejection layer that reflects or absorbs more than 50% of incident IR radiation. A second ETFE layer can be adhered to an inner surface of the structural polymer layer. The composite films are useful in structural applications and can withstand environmental exposure.

Description

    TECHNICAL FIELD
  • The present disclosure relates generally to multilayer polymer films. Specifically, the present disclosure relates to multilayer composite films for architectural applications.

  • BACKGROUND
  • Ethylene tetrafluoroethylene (ETFE) can be used in some architectural applications in place of conventional architectural glasses or plastics (e.g., tempered silicate glass, glass ceramics, polycarbonate). This is due, in part, to the light weight, visible light transparency and translucency, thermal stability, and flexibility exhibited by ETFE sheets. When used as a roofing material in architectural applications, ETFE is often either configured in a single layer that is supported by a network of cables or as a series of pneumatic cushions formed by joining of between two and five layers of ETFE together and inflating a space defined by the joined ETFE layers (and also sometimes supported by a network of cables).

  • Fabricating and maintaining a pneumatic cushion is currently an industry standard method of using ETFE for architectural elements. ETFE is extruded as a single sheet or a multi-layer sheet. ETFE sheets are joined together to form an envelope, which is then assembled into an architectural panel by attaching the envelope to a frame made from a structural material (e.g., aluminum, steel). The frame and the attached envelopes are in turn joined to supports of an architectural structure. The ETFE envelopes are inflated to form the pneumatic cushion. Pressure is maintained within the ETFE pneumatic cushions using a pressurization unit (such as a compressor) that maintains an internal pressure of the ETFE pneumatic cushions at approximately 220 Pa, thus providing structural stability to the pneumatic pillow.

  • SUMMARY
  • An example of the present disclosure includes a multilayer composite film including: an outer ethylene tetrafluoroethylene (ETFE) layer having a first major surface and a second major surface, the first major surface configured as an exterior surface of the multilayer composite film and the second major surface opposite the first major surface; a structural polymer layer proximate to the second major surface of the outer ETFE layer; a first fluoropolymer adhesive layer disposed between the second major surface of the outer ETFE layer and the structural polymer layer, the first fluoropolymer adhesive layer adhering the outer ETFE layer and the structural polymer layer together; a second ETFE layer having a first major surface and a second major surface, the first major surface of the second ETFE layer proximate to the structural polymer layer and the second major surface of the second ETFE layer configured as an interior surface opposite the first major surface of the outer ETFE layer; and a second fluoropolymer adhesive disposed between the first major surface of the second ETFE layer and the structural polymer layer, the second fluoropolymer adhesive layer adhering the second ETFE layer and the structural polymer layer together.

  • In an embodiment, the multilayer composite film further includes a fire retardant rating of V0 when tested according to a UL94 standard. In an embodiment, the multilayer composite film further includes an infra-red (IR) radiation rejection layer disposed in or on at least one of the structural polymer layer, the first fluoropolymer adhesive layer, the second fluoropolymer adhesive layer, and the outer ETFE layer, the IR radiation rejection layer configured to reflect at least 40% of incident IR radiation. In an embodiment of the multilayer composite film, wherein the IR radiation rejection layer includes a metal layer disposed on one of the structural polymer layer and the ETFE layer, the metal layer having a reflectance of greater than 40% for wavelengths of radiation between 700 nm and 1000 nm and having a transmittance of visible light having wavelengths between 400 nm and 700 nm greater than 50%. In an embodiment of the multilayer composite film, wherein the metal layer is one of a copper film, a silver film, a gold film, a nickel film, a metal oxide film, an aluminum film, and combinations thereof. In an embodiment of the multilayer composite film, wherein the metal layer has a thickness between 1 nm and 500 nm. In an embodiment of the multilayer composite film, wherein the IR radiation rejection layer includes at least one of titanium dioxide nanoparticles, silver particles, gold particles, and aluminum nanoparticles disposed in at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer. In an embodiment of the multilayer composite film, wherein the multilayer composite film has a young's modulus of at least 1000 MPa and an ultimate tensile strength of at least 146 MPa. In an embodiment of the multilayer composite film, wherein the multilayer composite film exhibits a yield point under tensile strain of at least 40 MPa. In an embodiment of the multilayer composite film, wherein the outer ETFE layer has a thickness of between 25 microns and 125 microns. In an embodiment of the multilayer composite film, wherein the second ETFE layer has a thickness from 25 microns to 125 microns. In an embodiment of the multilayer composite film, wherein the multilayer composite film where structural polymer layer is a polyethylene terephthalate (PET) layer. In an embodiment of the multilayer composite film, wherein multilayer composite film where the structural polymer layer has a thickness from 50 microns to 250 microns. In an embodiment of the multilayer composite film, wherein the multilayer composite film where at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer includes a fluoropolymer resin, an ultra-violet light absorbent component, and a crosslinking component. In an embodiment of the multilayer composite film, wherein the multilayer composite film where the fluoropolymer resin is at least 40 weight % of at least one of the first fluoropolymer layer and the second fluoropolymer layer. In an embodiment of the multilayer composite film, wherein the multilayer composite film where the fluoropolymer resin consists essentially of fluoropolymer-based polymers. In an embodiment of the multilayer composite film, wherein the multilayer composite film where at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer has a thickness from 5 microns to 30 microns. In an embodiment of the multilayer composite film, wherein the multilayer composite film further includes a perimeter edge configured to form a cord edge, where the second major surface of the second ETFE layer is adhered to itself using at least one of an adhesive and an adhesive tape. In an embodiment of the multilayer composite film, the multilayer composite film further including a rigid structure disposed within a volume defined by the cord edge. In an embodiment of the multilayer composite film, wherein the multilayer composite film has a haze value of less than 16%. In an embodiment of the multilayer composite film, wherein the multilayer composite film has a haze value of from 2% to 14%.

  • An example of the present disclosure includes a multilayer composite film including: an outer fluorinated polymer layer having a first major surface and a second major surface, the first major surface configured as an exterior surface of the multilayer composite film and the second major surface opposite the first major surface; a non-fluorinated polymer layer proximate to the second major surface of the outer fluorinated polymer layer; a first fluoropolymer adhesive layer disposed between the second major surface of the outer fluorinated polymer layer and the non-fluorinated polymer layer, the first fluoropolymer adhesive layer adhering the outer fluorinated polymer layer and the non-fluorinated polymer layer together; and a portion of the multilayer composite film defining an integral tube, the integral tube including a perimeter edge of the multilayer composite film curled back onto the multilayer composite film and permanently adhered to the multilayer composite film.

  • In an embodiment of the multilayer composite film, wherein the integral tube forms a cord edge. In an embodiment of the multilayer composite film, wherein the multilayer composite film further includes a first sheet of the multilayer composite film joined to a second sheet of the multilayer composite film. In an embodiment of the multilayer composite film, wherein the first sheet is joined to the second sheet using at least one of a lapp joint, a lapp joint and a strip, and a butt joint. In an embodiment of the multilayer composite film, wherein the first sheet is joined to the second sheet by at least one of an adhesive tape, an adhesive, and a heat seal. In an embodiment of the multilayer composite film, wherein the non-fluorinated polymer layer comprises PET. In an embodiment of the multilayer composite film, further including an IR reflecting layer or IR absorbing agent. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is an ETFE layer. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is a polyvinyl fluoride layer. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is an ethylene chlorotrifluoroethylene layer. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is a polyvinylidene fluoride layer. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is a polychlorotrifluoroethylene layer. In an embodiment of the multilayer composite film, wherein the outer fluorinated polymer layer is a polyfluoroethylenepropropylene layer.

  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1A

    is a cross-sectional view of an ETFE-containing multilayer composite film comprising a single ETFE layer, in an embodiment.

  • FIG. 1A

    ′ is a cross-sectional view of an ETFE-containing multilayer composite film comprising a single ETFE layer, in an embodiment.

  • FIG. 1B

    is a cross-sectional view of an ETFE-containing multilayer composite film that includes particles that can reflect and/or absorb IR radiation, in an embodiment.

  • FIG. 2

    . is a cross-sectional view of an ETFE-containing multilayer composite film comprising two layers of ETFE, in an embodiment.

  • FIG. 3

    is a graph of stress-strain data for both of an ETFE-containing multilayer composite film and a film comprising an ETFE bilayer.

  • FIG. 4

    is a graph of reflectance data for an ETFE-containing multilayer composite film, in an embodiment.

  • FIGS. 5A-5C

    illustrate various joint configurations for joining multilayer composite films together, in embodiments.

  • FIG. 6

    is a cross-sectional view of an ETFE-containing multilayer composite film configured for use as a structural panel, in another embodiment.

  • FIG. 7A

    is a cross-sectional view of an ETFE-containing multilayer composite film configured for use as a structural panel, in an embodiment.

  • FIG. 7B

    is a cross-sectional view of an ETFE-containing multilayer composite film configured for attachment to a support cable, in an embodiment.

  • The figures depict various embodiments of the present disclosure for purposes of illustration only. Numerous variations, configurations, and other embodiments will be apparent from the following detailed discussion.

  • DETAILED DESCRIPTION Overview
  • ETFE films have drawbacks that limit their applicability to architectural applications. For example, ETFE films have mechanical properties that do not generally lend themselves to use for structural elements of architectural applications. For example ETFE films generally have a low Young's modulus (about 800 MPa to about 1500 MPa) and have a relatively low yield point, after which the ETFE films deform elastically.

  • To overcome these properties, ETFE films are usually applied to architectural applications by configuring the ETFE film as a pneumatic cushion, as described above. An alternative embodiment uses single-ply ETFE panels that are supported by a network or grid of support cables that are separated by about one meter (m). Fabricating pneumatic cushions and maintaining pressure within the pneumatic cushions adds expense to the maintenance of the individual structural elements and the architectural application as a whole. Similarly, fabricating and maintaining a network of support cables adds expense to the use of ETFE as an architectural element and also detracts from the aesthetic appeal of the otherwise transparent ETFE architectural elements.

  • To improve the convenience with which ETFE films can be applied to architectural elements (e.g., roofs and walls), embodiments of the present disclosure include a multilayer composite film that includes an outer ETFE layer adhered to a structural polymer film, such as polyethylene terephthalate (PET), among others, by an adhesive. In some embodiments, the multilayer composite film may also include an infra-red (IR) radiation rejection layer that reflects at least 40% of incident IR radiation (light having a wavelength from 700 nm to 1000 nm), thus reducing the amount of IR radiation transmitted into an area defined, at least in part, by the optically transparent multilayer composite film. Variations and additional embodiments will be apparent upon reading the present disclosure.

  • Another advantage of using embodiments described herein as an architectural element is that the improved rigidity (from the flexural modulus of the structural polymer being higher than that of ETFE) and strength can increase the spacing (e.g., from the current 1 m spacing to at least 15 m) between support cables of a corresponding network, thus improving the visual appeal of ETFE architectural elements.

  • Yet another advantage of embodiments described herein is reduction in the haze in architectural elements using a multilayer composite film of the present disclosure compared to architectural components that currently use only ETFE. Current ETFE architectural components are about 250 μm thick. This thickness of ETFE has a visibly hazy appearance (measured according to ASTM D1003-13). Embodiments disclosed herein have a haze value of less than 20%, less than 16%, less than 12%, less than 10%, less than 8% and in some cases between 2% and 14% and in other cases about 6% (as measured according to ASTM D1003-13 using a BYK Gardner Haze Guard Plus haze meter). Embodiments described herein can include one or more layers of ETFE, each of which is as thin as 25 μm. A structural polymer layer used as a component of the multilayer composite film can be selected to have greater clarity (i.e., lower haze) than ETFE, thus further improving the visual clarity and aesthetic appearance of the architectural components using an embodiment of the multilayer composite film compared to single ply ETFE architectural components currently used.

  • Example Multilayer Composite Film
  • FIG. 1A

    is a cross-sectional view of an example

    multilayer composite film

    100, in an embodiment. The

    multilayer composite film

    100 includes an

    ETFE layer

    104, a

    structural polymer layer

    108, an adhesive 112, and an optional IR

    radiation rejection layer

    116. The

    multilayer composite film

    100 has a thickness, indicated by α in

    FIG. 1A

    , that can be within any of the following ranges: 50 to 1000 μm, 100 to 1000 μm, 200 to 1000 μm, 200 to 800 μm, 200 to 600 μm, greater than 100 μm, greater than 200 μm, greater than 500 μm, less than 3 mm, less than 2 mm, less than 1 mm, less than 800 μm, less than 500 μm, less than 400 μm or less than 300 μm.

  • The

    outer ETFE layer

    104 of the

    multilayer composite film

    100 is shown in this example as including a single sheet of ETFE material. In other examples, not shown, the

    ETFE layer

    104 can include multiple ETFE sheets to form the

    outer ETFE layer

    104. Other embodiments can include one, two, three or more ETFE sheets that may be separated by other layers of a composite film or may be adjacent each other (such as the example shown in

    FIG. 2

    and described below). The

    outer ETFE layer

    104 has a thickness, indicated by β in

    FIG. 1A

    , that can be, for example, within any of the following ranges: 25 microns (μm) to 250 μm; 25 μm to 100 μm; 25 μm to 75 μm; 25 μm to 50 μm; 50 μm to 150 μm; 50 μm to 100 μm; 75 μm to 200 μm; 75 μm to 100 μm; 100 μm to 200 μm. The

    outer ETFE layer

    104 is also shown as including a first major surface and a second major surface. These will be used for convenience to describe the structure and fabrication of the

    multilayer composite film

    100 in more detail below.

  • The

    outer ETFE layer

    104 is configured to be disposed as an exterior-facing surface of the

    multilayer composite film

    100. More specifically, for convenience of explanation, the first major surface of the

    outer ETFE layer

    104 can be used to form an exterior surface (i.e., exposed to the earth's atmosphere) of an architectural application. Placing the

    outer ETFE layer

    104 at an exterior surface employs many of the beneficial properties of ETFE material that may otherwise be lacking in more conventional architectural materials. For example, the low surface energy of ETFE helps shed water and resist accumulation of atmospherically born contaminants (e.g., soot, dirt, dust, pollen). ETFE, and more generally fluorinated polymers, can also exhibit resistance to solvation or other chemical degradation caused by atmospherically borne contaminants and chemicals intentionally applied (e.g., cleaners, detergents) and unintentionally applied (e.g., a spill) to an exterior surface of an architectural application. This low surface energy improves the longevity of the

    multilayer composite film

    100 because the film can resist chemically induced degradation. Furthermore, ETFE transmits as much as 90% or 95% of the intensity of incident visible light (e.g., radiation between wavelengths of 400 nanometers (nm) and 700 nm). This high transmissivity of ETFE is appealing in many architectural applications in which natural light is desired.

  • It will be appreciated that other fluorinated polymers may be substituted for the

    outer ETFE layer

    104, as well as other ETFE layers identified in other embodiments described below. Alternative fluorinated polymers include, but are not limited to, ethylene chlorotrifluoroethylene (ECTFE), polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF), polychlorotrifluoroethylene (PCTFE), and polyfluoroethylenepropropylene (FEP), perfluoroalkyl-tetrafluoroethylene (PFA), Lumiflon® (a copolymer of chlorotrifluoroethylene and modified hydroxyl-functionalized vinyl ethers and available from Asahi Glass Company, Ltd. of Tokyo, Japan), Zeffle® (a copolymer of tetrafluoroethylene and modified hydroxyl-functionalized vinyl esters and available from ® (available from Daikin Industries, Ltd. of Osaka, Japan), fluorinated polymethacrylates, fluorinated epoxy films, CTFE/VDF (chlorotrifluoroethylene-vinylidene fluoride copolymer), TFE/HFP (tetrafluoroethylene-hexafluoropropylene copolymer), HFP/VDF (hexafluoropropylene-vinylidene fluoride), TFE-PFMe (tetrafluoroethylene-perfluoromethylether copolymer), among others.

  • While the

    outer ETFE layer

    104 has many features advantageous for an exterior-facing surface of an architectural element, the mechanical properties (e.g., Young's modulus) of ETFE complicate the use of ETFE films alone in architectural applications. For at least this reason, the

    multilayer composite film

    100 includes at least one

    structural polymer layer

    108, as shown in

    FIG. 1A

    .

  • The

    structural polymer layer

    108 of the

    multilayer composite film

    100 adds structural integrity (e.g., higher Young's modulus, flexural modulus, ultimate tensile strength) to the

    multilayer composite film

    100 without compromising the benefits of the

    outer ETFE layer

    104 described above. One example of a polymer used for the

    structural polymer layer

    108 is polyethylene terephthalate (PET).

  • For example, ETFE can have a Young's modulus of approximately 800 MPa (mega pascals) to 1500 MPa, a flexural modulus of approximately 1.2 GPa (giga pascals), and an ultimate tensile strength of approximately 46 MPa (within normal measurement variation and natural variation between samples). In contrast, PET can exhibit a Young's modulus of approximately 2000 MPa to approximately 4000 MPa, a flexural modulus of approximately 8.3 GPa to approximately 14 GPa, and an ultimate tensile strength of approximately 60 MPa to approximately 140 MPa (within normal measurement variation and natural variation between samples).

  • Furthermore, in many embodiments the polymer selected for use as the

    structural polymer layer

    108 does not substantially decrease the transparency, translucence or clarity of the

    outer ETFE layer

    104 while at the same time improving the structural properties of the multilayer composite film, as explained above. The

    structural polymer layer

    108 can exhibit visible light transmission of greater than 40%, greater than 75%, greater than 85%, greater than 90% or greater than 95% at thicknesses of 25 μm, 50 μm, 100 μm, 150 μm, 200 μm, 300 μm, and 400 μm. When used in conjunction with the ETFE layer 104 (or with a

    second ETFE layer

    204 described below in the context of a multilayer composite film 200), the haze of the multilayer composite films of the present disclosure can be as low as from 2% to 16% (in some cases about 6%) and have visible light transmittances of as high (or higher) as 40%, 75%, 85%, 90%, or 95%. These improvements are present even for multilayer composite films having a comparable thickness to ETFE architectural films currently used (often as thick as 250 mm) because the

    structural polymer layer

    108 can be selected to have an equivalent or higher visible light transmittance than ETFE (or other fluoropolymers used in place of ETFE). Furthermore, because the

    structural polymer layer

    108 has improved mechanical properties over ETFE (and other fluoropolymers), the overall thickness of some embodiments of multilayer composite films can be reduced compared to ETFE architectural films currently used, thus further increasing the relative clarity and light transmittance of multilayer composite films described herein.

  • The

    structural polymer layer

    108 can have a thickness, indicated by x in

    FIG. 1A

    , that can be, for example, within any of the following ranges: 25 microns (μm) to 250 μm; 25 μm to 100 μm; 25 μm to 75 μm; 25 μm to 50 μm; 50 μm to 150 μm; 50 μm to 100 μm; 75 μm to 200 μm; 75 μm to 100 μm; 100 μm to 200 μm; greater than 50 μm, greater than 100 μm, greater than 150 μm, less than 2 mm, less than 1 mm, less than 800 μm, less than 500 μm, less than 300 μm or less than 200 μm. In part, the thickness of the

    structural polymer layer

    108 is selected based on the various material properties (e.g., Young's modulus, flexural modulus, ultimate tensile strength, among others).

  • Polymers other than PET can be used for the

    structural polymer

    108. Alternatives to PET include polymer films that have beneficial mechanical properties and high transmissivities to visible light. For example, the

    structural polymer layer

    108 can exhibit a Young's modulus of greater than 500 MPa, greater than 1000 MPa or greater than 4000 MPa and visible light transmission of greater than 40%, greater than 90%, greater than 95% or greater than 99% for a film having a thickness of 100 μm. The polymers can be extruded films or free-standing films that may include, but are not limited to: polypropylene, polyethylene, polyethylene vinyl acetate, polycarbonates, cellulose and cellulose derivatives, polyamide-imide, polyurethanes, polyacrylates, polymethacrylates, polythiophenes, poly(3,4-ethylenedioxythio-phene)/polystyrene sulfonate, polystyrene, biopolymers, fluoropolymers, chlorofluoropolymers, vinylfluoropolymers, poly (vinyl chloride), polyethers, polyimides, polyetherimides, polyphenylsulfone, and combinations thereof.

  • The adhesive 112 of the

    multilayer composite film

    100 is used to join the

    structural polymer layer

    108 to the second major surface of the

    outer ETFE layer

    104, as shown in

    FIG. 1A

    . The adhesive can be a

    fluoropolymer adhesive

    112 that has high thermal stability, hydrolysis resistance, and UV stability. These properties facilitate long term adhesion between the

    structural polymer layer

    108 and the

    outer ETFE layer

    104 even when subjected to months and years of solar-induced heating and solar irradiation, respectively. Furthermore, the strength of adhesion between the

    structural polymer layer

    108 and the

    outer ETFE layer

    104 provided by the

    fluoropolymer adhesive

    112 can, in some embodiments, be within any of the following ranges: from 1 Newton (N)/centimeter (cm) to 10 N/cm; from 1 N/cm to 5 N/cm; from 1 N/cm to 3 N/cm; from 2 N/cm to 10 N/cm; from 2 N/cm to 7 N/cm; from 3 N/cm to 7 N/cm; from 5 N/cm to 10 N/cm; from 5 N/cm to 10 N/cm; greater than 3 N/cm, greater than 5 N/cm or greater than 7 N/cm. The

    fluoropolymer adhesive

    112 has a thickness, indicated by δ in

    FIG. 1A

    , that can be within any of the following ranges: 2 μm to 50 μm; 2 μm to 30 μm; 5 μm to 30 μm; 10 μm to 30 μm; 15 μm to 30 μm. Examples of fluoropolymer resins used as a component of the

    fluoropolymer adhesive

    112 include fluoro-copolymer resins and fluoropolymer resins that are terpolymers. Other example fluoropolymer resins used as a component of the

    fluoropolymer adhesive

    112 include, but are not limited to, perfluoroalkyl vinyl ethers such as Lumiflon® (available from Asahi Glass Company, Ltd. of Tokyo, Japan) and tetrafluoroethylene based copolymers, such as Zeffle® (available from Daikin Industries, Ltd. of Osaka, Japan). In some embodiments, the

    fluoropolymer adhesive

    112 may be free of adhesives other than fluoropolymers (e.g., free of acrylic, polyol and other adhesives).

  • In other embodiments, the

    fluoropolymer adhesive

    112 includes one or more non-fluorinated components in addition to the fluorinated resin component. In one example, the

    fluoropolymer adhesive

    112 includes an amine or hydroxyl polyol fluorinated resin. In another example, the

    fluoropolymer adhesive

    112 may include a polyester polyol adhesive component, such as Adcote 76R40 (available from Rohm and Haas of Philadelphia, Pa., United States).

  • Other elements that can be included in the

    fluoropolymer adhesive

    112 composition include a UV absorber that improves the stability of the

    fluoropolymer adhesive

    112 and underlying layers upon exposure to light include nitroxy radical based compounds, among others. UV absorbers that can be added to the

    fluoropolymer adhesive

    112 include Uvinul 3050, Tinuvin® 400, Tinuvin® 477, Tinuvin® 479, Tinuvin® 384-2, Tinuvin® 1600, Tinuvin® P, Tinuvin® CarboProtect, Tinuvin® 5000 series (all of which are available from BASF of Ludwigshafen, Germany), Evesorb 74 (from Everlight Chemical of Taipei, Taiwan), and inorganic UV absorbers such as zinc oxide, cerium oxide, titanium dioxide, and transparent iron oxides. The

    fluoropolymer adhesive

    112 composition may also include a hindered amine light stabilizer (HALS) to further improve resistance to UV light degradation and improve the performance of an included UV light absorber. Examples of HALS include but are not limited to Tinuvin® 123, Tinuvin® 171 (which are available from BASF), and combinations thereof. Flame retardants, which may also be included as a component in the

    fluoropolymer adhesive

    112 composition include non-halogenated flame retardants such as Exolit® OP550, Exolit® OP560 (both of which are available from Clariant Manufacturing Company of Muttenz, Switzerland), Levagard®4090N (available from Rhein Chemie of Mannheim, Germany), or mixtures thereof.

  • Organic solvents that may be used for the synthesis of the

    fluoropolymer adhesive

    112 include but are not limited to organic solvents such as methyl ethyl ketone (MEK), acetone, methyl isobutyl ketone (MIBK), toluene, xylene, methanol, heptane, ethyl acetate, isopropyl acetate, n-butyl acetate, or mixtures thereof. The adhesive compositions of various embodiments can be applied to polymeric film by any of a variety of methods known to those skilled in the art of film coating manufacture. Suitable application methods include application by Meyer rod coating, comma coating, spraying, slot die coating, curtain coating, dipping and/or brushing.

  • In some examples, the

    fluoropolymer adhesive

    112 can be prepared by mixing a fluoropolymer resin and a crosslinking agent in an organic solvent. Other components, such as ultra-violet (UV) radiation absorbing compounds, IR reflective and/or absorbing compounds, among others, can also be added to the organic solvent. In one example, the following mixture can be assembled: 50 parts to 200 parts by weight of fluoropolymer resin; 2 parts to 20 parts by weight of UV absorber; 5 parts to 40 parts by weight of organic solvent; 5 parts to 40 parts by weight of crosslinking agent. These are then thoroughly mixed. After removal of the solvent (e.g., by evaporation, vacuum assisted evaporation, heating assisted evaporation), the now crosslinked adhesive composition may comprise at least 20%, at least 30% at least 40%, at least 50%, at least 60%, at least 70%, at least 80%, or at least 90% fluoropolymer by weight. An example formulation of

    fluoropolymer adhesive

    112 follows in Table 1.

  • TABLE 1
    Weight
    Component Name (Supplier) Function (grams (g))
    Zeffle ® GK 570 (Daikin) Fluoropolymer component 100
    Tinuvin ® 384-2 (BASF) UV absorber 4.4
    Desmodur ® N 3800 (Bayer) Crosslinking agent 20
    Methyl ethyl ketone (N/A) Organic solvent 80
  • Optional IR

    radiation rejection layer

    116 of the

    multilayer composite film

    100 may actually include one or both of IR reflecting materials and IR absorbing materials. The IR

    radiation rejection layer

    116 reduces the amount of IR radiation passing through the

    multilayer composite film

    100, thus reducing the IR-induced heating of the interior spaces within an architectural structure. Similarly, IR absorbing materials absorb infrared radiation in the film composite and prevent much of the incident IR radiation from reaching the interior of the structure. This in turn reduces the cooling needed for these interior spaces, improving the economic and ecological performance of the architectural structure using the

    multilayer composite film

    100. The IR

    radiation rejection layer

    116 has a thickness, indicated by ε in

    FIG. 1A

    that can be within any of the following ranges: from 1 nm to 100 nm; from 10 nm to 50 nm; from 50 nm to 100 nm; from 25 nm to 75 nm; from 25 nm to 50 nm; and from 50 nm to 75 nm.

  • The example of the IR

    radiation rejection layer

    116 shown in

    FIG. 1A

    is that of a metal film (alternatively referred to as a metal layer) deposited onto a surface of the

    structural polymer layer

    108. The metal layer of the IR

    radiation rejection layer

    116 may also include multiple layers of metal. The IR

    radiation rejection layer

    116 on the

    structural polymer layer

    108 can be adhered to the second major surface of the

    outer ETFE layer

    104 via the

    fluoropolymer adhesive

    112. Metal films can be continuous or be fabricated to include a pattern of metal portions and non-metal portions (often referred to as a “frit pattern”). Examples of metals used to form a metal film for the IR radiation rejection layer 116 (deposited via, e.g., sputtering, physical vapor deposition, evaporation, among others) include, but are not limited to, aluminum, silver, copper, gold, metal oxides, combinations thereof, or other suitable metals or intermetallic compounds having an electronic structure that reflects at least 40% of incident IR radiation present in solar radiation. Sputtered metallic films can exhibit surface energies that facilitate adhesion to an opposed layer.

  • In other embodiments, such as the one shown in

    FIG. 1A

    ′, the IR

    radiation rejection layer

    116 can be adhered to the

    outer ETFE layer

    104 directly. In some embodiments,

    fluoropolymer adhesive layer

    112 and IR

    radiation rejection layer

    116 may be transposed from the figure so that the IR rejection layer is

    adjacent layer

    104 and the adhesive layer is

    adjacent layer

    108. In another alternative embodiment

    multilayer composite film

    120 shown in

    FIG. 1B

    , the separate fluoropolymer

    adhesive layer

    112 and IR

    radiation rejection layer

    116 are substituted for a single

    fluoropolymer adhesive layer

    124 that also includes

    particles

    128 that absorb and/or block IR radiation. This layer has a thickness ε′ that can be in any of the ranges already introduced above as thickness δ, thickness ε, or combinations thereof. Examples of IR blocking materials (or “IR opaque pigments”) include Sicopal® Black K 0095 from BASF and nanoparticles (e.g., titanium dioxide nanoparticles, silver nanoparticles, aluminum nanoparticles, and mixtures thereof).

  • In other examples, the

    particles

    128 include those that alternate between reflecting IR radiation at high atmospheric temperatures (e.g., above 60° F.) and transmitting IR radiation at low atmospheric temperatures (e.g., below 50° F.).

  • Other embodiments of the IR

    radiation rejection layer

    116 and the fluoropolymer adhesive/

    IR layer

    124 may include IR reflective dyes, IR absorbent dyes, UV absorbent dyes, light stabilizers, antioxidants, flame retardants, and mixtures thereof, in examples. Flame retardants may be added to any of the embodiments described herein to provide a flame resistance rating of V0 as measured according to the Underwriters Laboratories (UL) standard UL94, edition number 6, dated Mar. 28, 2013. Embodiments described herein may also meet other fire related standards such as National Fire Protection Association (NFPA) standard 701, 2015 edition, and ASTM standard E84-16 for “Surface Burning Characteristics of Building Materials.” Furthermore, absent additional flame retardants, embodiments such as the multilayer composite film 100 (described above), multilayer composite film (200), as well as various combinations that include multiple layers of any one or more of the

    individual layers

    104, 108, 112, 116, 124, and 204 may be configured to comply with one or more of UL standard UL94, edition number 6, dated Mar. 28, 2013, National Fire Protection Association (NFPA) standard 701, 2015 edition, and ASTM standard E84-16 for “Surface Burning Characteristics of Building Materials.”

  • Regardless of the selection or composition of the IR

    radiation rejection layer

    116 and the fluoropolymer adhesive/

    IR layer

    124, the

    multilayer composite film

    100 can still retain most of or all of the optical light transmissivity described above and is not only translucent but also transparent.

  • ALTERNATIVE EMBODIMENTS
  • FIG. 2

    illustrates an ETFE

    multilayer composite film

    200 that includes the

    multilayer composite film

    100 and a

    second ETFE layer

    204 attached to a surface of the

    structural polymer layer

    108 opposite that of the

    outer ETFE layer

    104. The

    second ETFE layer

    204, configured to be disposed on as a surface on an interior of an architectural structure opposite the exterior surface, has a thickness, indicated in

    FIG. 2

    by γ, within any of the following ranges: 25 microns (μm) to 250 μm; 25 μm to 100 μm; 25 μm to 75 μm; 25 μm to 50 μm; 50 μm to 150 μm; 50 μm to 100 μm; 75 μm to 200 μm; 75 μm to 100 μm; 100 μm to 200 μm. A second

    fluoropolymer adhesive layer

    114 that can have the same dimensions and composition as the

    fluoropolymer adhesive layer

    112 and/or a fluoropolymer adhesive/IR layer 124 (shown only in

    FIG. 1B

    ) may be disposed between the

    second ETFE layer

    204 and the

    structural polymer layer

    108. IR reflectors or absorbents and other particles or dyes can be disposed in or adjacent to any of the

    adhesive layers

    112, 114 that are used to join opposed polymer films. These layers have been described above and need no further description.

  • EXPERIMENTAL EXAMPLE
  • Example composite films were prepared according to the following procedure. A solution of fluoropolymer-based adhesive was prepared according to the formulation described above in Table 1. The prepared fluoropolymer-based adhesive solution was applied to a 125 m thick PET (V0 fire rating per UL94) film, which functioned as the structural polymer layer described above, at a coating weight of 15 g/m2. A first 25 μm thick ETFE film was laminated onto the fluoropolymer-based adhesive bearing PET film. The fluoropolymer-based adhesive was then applied on the opposite side of the PET film at a coating weight of 15 g/m2 and then laminated with a second 25 μm thick ETFE film.

  • The prepared experimental examples were subjected to uniaxial testing using an INSTRON 3360 dual column testing system. The experimental examples were strained at a uniform strain rate of 50 millimeters/minute. The stress-strain curve of the experimental example appears in

    FIG. 3

    along with a comparison to a 250 μm thick sheet of ETFE control sample that was strained separately but used the same uniaxial testing machine and strain rate identified above.

  • As apparent upon inspection of the data presented in the graph of

    FIG. 3

    , the experimental example exhibits significantly higher Young's modulus than the ETFE alone. The experimental example also exhibits a single yield point at about 5% strain (at a stress of about 70 MPa) and had an ultimate yield stress of approximately 146 MPa (within normal measurement tolerances and natural variation within a population of samples).

  • The experimental example was also subjected to 96 hours of highly accelerated stress testing (HAST) to test the adhesion between the layers. The HAST testing was performed at 121° C., 100% Relative Humidity (RH) and 1 atm. The experimental example was also tested using the Damp Heat Test (International Electrochemical Commission standard number IEC60721) at 85 C, 85% (RH), for 1000 hours. Despite the known difficulties of adhering ETFE to dissimilar polymers, no delamination, blistering, or cracking was observed at the end of 96 hours of HAST testing or at the end of 1000 hours for the Damp Heat Test. This confirms that the fluoropolymer-based adhesive strongly adheres the PET film to the ETFE film. The experimental example was also subjected to the Vertical Burning test and exhibited self-extinguishing behavior.

  • FIG. 4

    illustrates a graph of reflectance data exhibited by an experimental example of a multilayer composite film of the present disclosure fabricated from two layers of ETFE film between which was adhered a layer of Vikuiti™ film. The experimental sample was exposed to incident light having a plurality of wavelengths approximating a solar light wavelength distribution. IR reflectance data was collected using a PERKIN ELMER 950 spectrophotomer. These results are shown in

    FIG. 4

    . As is shown, IR reflectance is approximately 100% for IR wavelengths from approximately 780 nm to approximately 1000 nm. At the same time, reflectance in the visible range was less than 20%.

  • Example Configurations for Architectural Application
  • FIGS. 5A-5C

    illustrate various joints that can be used for joining multilayer composite films together, in embodiments. The joints enable individual sheets of multilayer composite films of the present disclosure to be joined together into a larger architectural panel. For example, individual sheets can be joined together to produce an architectural panel that is, for example, anywhere from 1×1 m to 25×25 m square before requiring external support (such as from a network of support cables).

    FIG. 5A

    illustrates a lap joint in which individual sheets of the

    multilayer composite film

    200 are overlapped by a distance designated in

    FIG. 5A

    as a seal width. The individual sheets can be joined using, for example, a heat seal that welds the sheets together, or an adhesive tape (e.g., a polyester base or a polyamide base thermoplastic heat activated adhesive tape) or an adhesive (e.g., a heat activated adhesive) disposed between the overlapping portions of the individual sheets of the

    multilayer composite film

    200.

  • FIG. 5B

    illustrates a butt joint in which proximate perimeter edges of two sheets of multilayer

    composite films

    200 are butted together end-to-end and joined at the seal indicated using, for example, any of the techniques described above in the context of

    FIG. 5A

    .

    FIG. 5C

    illustrates a variation of the butt joint shown in

    FIG. 5B

    . In

    FIG. 5C

    , a

    strip

    504 of single layer film or multilayer composite film 200 (or ETFE or other compatible polymer used as an outer layer 104) is joined to one or optionally both of the major surfaces of the sheets of multilayer

    composite films

    200 joined via a butt joint so as to cover and extend beyond the butt joint. It will be appreciated that the multilayer

    composite films

    100, 118, and 120 may be substituted for any of the films and/or strips shown in

    FIGS. 5A, 5B, and 5C

    . An adhesive, for example a fluoropolymer adhesive such as a perfluoroalkyl vinyl ether, may be used in one or more of the seals between the polymer composite films or between the polymer composite film and one or more of

    strip

    504. The tensile strength of these joints may be equal to, or better than, the tensile strength of the composite film itself.

  • In any of the above figures, a seal width can be in any of the following ranges: from 0.5 cm to 10 cm; from 0.5 cm to 5 cm; from 0.5 cm to 2.5 cm; from 1 cm to 10 cm; from 1 cm to 5 cm; from 2 cm to 7 cm, greater than 1.0 cm, or less than 10 cm.

  • FIG. 6

    illustrates another embodiment of a

    multilayer composite film

    200 configured to form a “cord edge” 500 that defines a volume and is formed by curling the

    multilayer composite film

    200 around a rigid cord (such as EPDM rubber) that is then slid into a channel of a retaining structure. In various embodiments the structure may be erected before or after the cord edge is inserted into the channel. The retaining structure can be attached or anchored (directly or indirectly) to the structure of the building or architectural application in which the

    multilayer composite film

    200 is used as an element. In the embodiment illustrated, the second major surface is adhered to itself to form the

    cord edge

    500. The

    cord edge

    500 may be inserted into the structural channel prior to sealing the composite. For instance, the cord and cord edge may be inserted into the channel and the seal region then clamped and sealed. In other cases, the cord edge is sealed around the cord and is then slid into the channel to secure the composite film to the structure. In one example, a first major surface may be fabricated from a different material than the second major surface because the first and second major surfaces need not be adhered together. For instance, the second major surface can be a fluoropolymer such as perfluoroalkyl vinyl ether and first major surface can be a non-fluorinated polymer including polyethyleneterephthalate-based materials such as PET. In these embodiments, the second major surface may be the side of the composite that is exposed to the environment. As in the example of

    FIG. 6

    , the composite film can be adhered to itself using an adhesive, an adhesive tape or by welding, such as polymer welding, heat welding or ultrasonic welding. Adhesives can include, for example, fluorinated polymers such as perfluoroalkyl vinyl ether.

  • FIG. 7A

    illustrates an example of the

    multilayer composite film

    200 configured for use as an architectural element. In this example, one perimeter edge of the

    multilayer composite film

    200 has been curled so that the second major surface of the

    second ETFE layer

    204 contacts the first major surface of the

    outer ETFE layer

    104. The two

    ETFE layers

    204 may then be joined (e.g., using an adhesive, adhesive tape, or by heat sealing) around a cord to form the

    cord edge

    500 as described above. In another embodiment, the composite film can be rolled onto itself to form a cord edge in which the space typically occupied by a cord is filled by spiraled composite film material.

  • FIG. 7B

    illustrates an alternative configuration for attaching a sheet or panel of the

    multilayer composite film

    200 to a support cable. In this example a

    strip

    704 of either ETFE or of the

    multilayer composite film

    200 is sealed to the sheet and/or panel of multiple sheets of the

    multilayer composite film

    200 around a

    support cable

    708. The seal widths indicated in

    FIG. 7B

    can be on the order of those described above. The same or similar sealing and adhesion techniques can be used.

  • It will be appreciated that the multilayer

    composite films

    100, 118, and 120 may be substituted for any of the films and/or strips shown in

    FIGS. 6, 7A, and 7B

    .

  • Further Considerations
  • The foregoing description of the embodiments of the disclosure has been presented for the purpose of illustration; it is not intended to be exhaustive or to limit the claims to the precise forms disclosed. Persons skilled in the relevant art can appreciate that many modifications and variations are possible in light of the above disclosure.

  • The language used in the specification has been principally selected for readability and instructional purposes, and it may not have been selected to delineate or circumscribe the inventive subject matter. It is therefore intended that the scope of the disclosure be limited not by this detailed description, but rather by any claims that issue on an application based hereon. Accordingly, the disclosure of the embodiments is intended to be illustrative, but not limiting, of the scope of the invention, which is set forth in the following claims.

Claims (35)

What is claimed is:

1. A multilayer composite film comprising:

an outer ethylene tetrafluoroethylene (ETFE) layer having a first major surface and a second major surface, the first major surface configured as an exterior surface of the multilayer composite film and the second major surface opposite the first major surface;

a structural polymer layer proximate to the second major surface of the outer ETFE layer;

a first fluoropolymer adhesive layer disposed between the second major surface of the outer ETFE layer and the structural polymer layer, the first fluoropolymer adhesive layer adhering the outer ETFE layer and the structural polymer layer together;

a second ETFE layer having a first major surface and a second major surface, the first major surface of the second ETFE layer proximate to the structural polymer layer and the second major surface of the second ETFE layer configured as an interior surface opposite the first major surface of the outer ETFE layer; and

a second fluoropolymer adhesive layer disposed between the first major surface of the second ETFE layer and the structural polymer layer, the second fluoropolymer adhesive layer adhering the second ETFE layer and the structural polymer layer together.

2. The multilayer composite film of

claim 1

, further comprising a fire retardant rating of V0 when tested according to a UL94 standard.

3. The multilayer composite film of

claim 1

, further comprising an infra-red (IR) radiation rejection layer disposed in or on at least one of the structural polymer layer, the first fluoropolymer adhesive layer, the second fluoropolymer adhesive layer, and the outer ETFE layer, the IR radiation rejection layer configured to reflect at least 40% of incident IR radiation.

4. The multilayer composite film of

claim 3

wherein the IR radiation rejection layer comprises a metal layer disposed on one of the structural polymer layer and the outer ETFE layer, the metal layer having a reflectance of greater than 40% for wavelengths of radiation between 700 nm and 1000 nm and having a transmittance of visible light having wavelengths between 400 nm and 700 nm greater than 50%.

5. The multilayer composite film of

claim 4

, wherein the metal layer is one of a copper film, a silver film, a gold film, a nickel film, a metal oxide film, an aluminum film, and combinations thereof.

6. The multilayer composite film of

claim 4

, wherein the metal layer has a thickness between 1 nm and 500 nm.

7. The multilayer composite film of

claim 3

, wherein the IR radiation rejection layer comprises at least one of titanium dioxide nanoparticles, silver particles, gold particles, and aluminum nanoparticles disposed in at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer.

8. The multilayer composite film of any one of

claims 1

-

3

, wherein the multilayer composite film has a Young's modulus of at least 1000 MPa and an ultimate tensile strength of at least 146 MPa.

9. The multilayer composite film of

claim 8

, wherein the multilayer composite film exhibits a yield point under tensile strain of at least 40 MPa.

10. The multilayer composite film of any one of

claims 1

-

3

, wherein the outer ETFE layer has a thickness of between 25 microns and 125 microns.

11. The multilayer composite film of any one of

claims 1

-

3

, wherein the second ETFE layer has a thickness from 25 microns to 125 microns.

12. The multilayer composite film of any one of

claims 1

-

3

, wherein structural polymer layer is a polyethylene terephthalate (PET) layer.

13. The multilayer composite film of any one of

claims 1

-

3

, wherein the structural polymer layer has a thickness from 50 microns to 250 microns.

14. The multilayer composite film of any one of

claims 1

-

3

, wherein at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer includes a fluoropolymer resin, an ultra-violet light absorbent component, and a crosslinking component.

15. The multilayer composite film of

claim 14

, wherein the fluoropolymer resin is at least 40 weight % of at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer.

16. The multilayer composite film of

claim 15

, wherein the fluoropolymer resin consists essentially of fluoropolymer-based polymers.

17. The multilayer composite film of any one of

claims 1

-

3

, wherein at least one of the first fluoropolymer adhesive layer and the second fluoropolymer adhesive layer has a thickness from 5 microns to 30 microns.

18. The multilayer composite film of any one of

claims 1

-

3

, further comprising a perimeter edge configured to form a cord edge, wherein the second major surface of the second ETFE layer is adhered to itself using at least one of an adhesive and an adhesive tape.

19. The multilayer composite film of

claim 18

, further comprising a rigid structure disposed within a volume defined by the cord edge.

20. The multilayer composite film of any one of

claims 1

-

3

, further comprising a haze value of less than 16%.

21. The multilayer composite film of any one of

claims 1

-

3

, further exhibiting a haze value of from 2% to 14%.

22. A multilayer composite film comprising:

an outer fluorinated polymer layer having a first major surface and a second major surface, the first major surface configured as an exterior surface of the multilayer composite film and the second major surface opposite the first major surface;

a non-fluorinated polymer layer proximate to the second major surface of the outer fluorinated polymer layer;

a first fluoropolymer adhesive layer disposed between the second major surface of the outer fluorinated polymer layer and the non-fluorinated polymer layer, the first fluoropolymer adhesive layer adhering the outer fluorinated polymer layer and the non-fluorinated polymer layer together; and

a portion of the multilayer composite film defining an integral tube, the integral tube comprising a perimeter edge of the multilayer composite film curled back onto the multilayer composite film and permanently adhered to the multilayer composite film.

23. The multilayer composite film of

claim 22

, wherein the integral tube forms a cord edge.

24. The multilayer composite film of

claim 22

, further comprising a first sheet of the multilayer composite film joined to a second sheet of the multilayer composite film.

25. The multilayer composite film of

claim 24

, wherein the first sheet is joined to the second sheet using at least one of a lap joint, a lap joint and a strip, and a butt joint.

26. The multilayer composite film of

claim 24

or

25

, wherein the first sheet is joined to the second sheet by at least one of an adhesive tape, an adhesive, and a heat seal.

27. The multilayer composite film of any one of

claims 22

-

24

, wherein the non-fluorinated polymer layer comprises PET.

28. The multilayer composite film of

claim 27

, further comprising an IR reflecting layer or IR absorbing agent.

29. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is an ETFE layer.

30. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is a polyvinyl fluoride layer.

31. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is an ethylene chlorotrifluoroethylene layer.

32. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is a polyvinylidene fluoride layer.

33. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is a polychlorotrifluoroethylene layer.

34. The multilayer composite film of any one of

claims 22

-

24

, wherein the outer fluorinated polymer layer is a polyfluoroethylenepropropylene layer.

35. An architectural structure comprising the composite film of any one of the preceding claims.

US15/772,236 2015-10-28 2016-10-28 Multilayer composite films for architectural applications Abandoned US20180311943A1 (en)